Quantum cascade laser (QCL) enduring high temperature continuous-wave (CW) operation is of paramount importance to address their application in gas sensing. We report on the realization of lattice-matched InGaAs/InAlAs/InP QCL materials grown by metal-organic chemical vapor deposition (MOCVD). High-quality interface structure designed for light emission at 8.5 μm was achieved by optimizing and precise controlling of growth conditions. A CW output power of 1.04 W at 288 K was obtained from a 4 mm-long and 10 μm-wide coated laser. Corresponding maximum wall-plug efficiency and threshold current density were 7.1% and 1.18 kA/cm². The device can operate in CW mode up to 408 K with an output power of 160 mW, which demonstrates excellent temperature stability.

Nonlocal wavelength-to-time mapping between frequency entangled photon pairs generated with the process of spontaneous parametric down-conversion is theoretically analyzed and experimentally demonstrated. The spectral filtering pattern experienced by one photon in the photon pair will be non-locally mapped into the time domain when the other photon propagates inside a dispersion-compensation fiber with large group velocity dispersion. Our work, for the first time, points out that the spectral bandwidth of the pump laser will become the dominated factor preventing the improvement of the spectral resolution when the involved group velocity dispersion is large enough, which provides an excellent tool of characterizing the resolution of a nonlocal wavelength-to-time mapping for further quantum information applications.